鋅合金特性
| 壓鑄鋅合金國際標準成份 | ||||||||
| 通用牌號 |
No.2(%) |
No.3(%) |
No.4(%) |
No.5(%) |
No.7(%) |
ZA-8(%) |
ZA-12(%) |
ZA-27(%) |
|
鋁 (Al) |
3.9-4.3 |
3.9-4.3 |
3.9-4.32 |
3.9-4.3 |
3.9-4.3 |
8.2-8.8 |
10.8-11.5 |
25.5-28.0 |
| 鎂 (Mg) |
0.025-0.05 |
0.025-0.05 |
0.025-0.05 |
0.03-0.06 |
0.010-0.02 |
0.020-0.030 |
0.020-0.030 |
0.012-0.020 |
|
銅 (Cu) |
2.6-2.9 |
0.10max |
0.3-0.4max |
0.75-1.25 |
0.10max |
0.8-1.3 |
0.5-1.2 |
2.0-2.5 |
|
鉛 (Pb) |
0.004max |
0.004max |
0.004max |
0.004max |
0.002max |
0.005max |
0.005max |
0.005max |
|
鎘 (Cd) |
0.003max |
0.003max |
0.003max |
0.003max |
0.002max |
0.005max |
0.005max |
0.005max |
|
鍚 (Sn) |
0.002max |
0.002max |
0.002max |
0.002max |
0.001max |
0.002max |
0.002max |
0.002max |
|
鐵 (Fe) |
0.075max |
0.075max |
0.075max |
0.075max |
0.075max |
0.065max |
0.065max |
0.072max |
|
鎳 (Ni) |
- |
- |
- |
- |
0.005-0.020 |
- |
- |
- |
|
鋅 (Zn) |
餘量 |
餘量 |
餘量 |
餘量 |
餘量 |
餘量 |
餘量 |
餘量 |
| 鋅合金物理特性 | ||||||||
| 通用牌號 |
No.2(%) |
No.3(%) |
No.4(%) |
No.5(%) |
No.7(%) |
ZA-8(%) |
ZA-12(%) |
ZA-27(%) |
|
密度 (g/cm) |
6.6 |
6.6 |
6.6 |
6.6 |
6.6 |
6.3 |
6.0 |
5.0 |
| 溶點 (C) |
379-390 |
381-387 |
380-386 |
380-386 |
381-387 |
375-404 |
377-432 |
376-484 |
|
電導率 (%IACS) |
25 |
27 |
26-27 |
26 |
27 |
27.7 |
28.3 |
29.7 |
|
熱傳導率 (100c,W/m.k) |
104.7 |
113 |
180.9-113.0 |
108.9 |
11.3 |
114.7 |
116.1 |
125.5 |
|
熬膨脹系數 |
27.8 |
27.4 |
27.4 |
27.4 |
27.4 |
23.3 |
24.2 |
26.0 |
|
比熱 (J/kg.k) |
418.7 |
418.7 |
418.7 |
418.7 |
418.7 |
435.4 |
448.0 |
534.4 |
|
縮模率 (mm/mm) |
0.006 |
0.006 |
0.007 |
0.006 |
0.006 |
0.007 |
0.0075 |
0.008 |
| 鋅合金機械特性 | |||||||||||
| 通用牌號 |
No.2(%) |
No.3(%) |
No.4(%) |
No.5(%) |
No.7(%) |
ZA-8(%) |
ZA-12(%) |
ZA-27(%) |
|||
|
機械特性 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
壓鑄 |
|
極限抗拉強度(Mpa) |
359 |
283 |
317 |
331 |
283 |
372 |
248-276 |
400 |
276-317 |
421 |
400-440 |
|
沖擊應力 (J) |
47 |
58 |
61 |
65 |
58 |
42 |
20 |
28 |
25 |
- |
47 |
|
延伸系數 (%) |
7 |
10 |
7 |
7 |
13 |
6-10 |
1-2 |
4-7 |
1-3 |
1-3 |
3-6 |
|
布氏硬度 (HB) |
100 |
82 |
92 |
91 |
80 |
95-110 |
80-90 |
95-115 |
90-105 |
105-125 |
110-120 |
|
抗剪強度 (MPa) |
317 |
214 |
214-262 |
262 |
262 |
275 |
- |
275 |
- |
296 |
255 |
|
屈服強度(0.2%,MPa) |
- |
- |
221-269 |
- |
- |
290 |
200 |
317 |
207 |
365 |
365 |
|
抗勞損強度 |
58.6 |
47.6 |
48-57 |
56.5 |
- |
- |
- |
- |
103.5 |
- |
172.5 |
|
壓力屈服強度(0.1%m,MPa) |
641 |
414 |
414-600 |
600 |
600 |
252 |
199 |
252 |
199 |
269 |
227 |
鋅合金壓鑄模之優點：
．產品可獲得較高之尺寸精度
．模具壽命可達20萬模次以上
．可降低後加工機製比例
．適合大量生產
鋅合金壓鑄品的特性及優點：
．極佳的機械價值
．成品尺寸穩定度高及精確度佳 ( 可至 0.03 毫米 )
．具極佳的表面品質，可避免附加的表面處理程式
．薄壁部分的高抗拉性極佳
．低生產成本
．透過熱室鑄造具高生產比率
．透過簡單的生產過程產生較低的投資成本
．架模成本低
．彈性的生產速度：低速，一般，或高速的生產速度皆有可能
．極佳的防腐蝕特性
Copyright © PENG MING ENTERPRISE CO.,LTD All Rights Reserved.Designed by EBM